Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density | | ASTMD792 | 1.05 | g/cm³ |
| Density | 23°C | ISO1183 | 1.05 | g/cm³ |
| Melt Mass-Flow Rate | 200°C/5.0kg | ASTMD1238 | 1.9 | g/10min |
| Melt Mass-Flow Rate | 220°C/10.0kg | ASTMD1238 | 19 | g/10min |
| Melt Mass-Flow Rate | 200°C/5.0kg | ISO1133 | 1.9 | g/10min |
| Melt Mass-Flow Rate | 220°C/10.0kg | ISO1133 | 19 | g/10min |
| Modeling Shrinkage | MD | 内部方法 | 0.40to0.70 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Strength | 23°C | ASTMD638 | 47.6 | Mpa |
| Tensile Stress | 屈服,23°C | ISO527-2 | 48.0 | Mpa |
| Flexural Modulus | 23°C | ASTMD790 | 2650 | Mpa |
| Flexural Modulus | 23°C | ISO178 | 2650 | Mpa |
| Flexural Strength | 23°C | ASTMD790 | 79.4 | Mpa |
| Flexural Stress | 23°C | ISO178 | 79.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat Softening Temperature | | ASTMD15253 | 100 | °C |
| Vicat Softening Temperature | | ISO306/A | 100 | °C |
| Heat Deflection Temperature | 1.8MPa,退火 | ISO75-2/A | 95.0 | °C |
| Heat Deflection Temperature | 1.8MPa,未退火,12.7mm | ASTMD648 | 85.0 | °C |
| Heat Deflection Temperature | 1.8MPa,Unannealed,12.7mm | ISO75-2/A | 85.0 | °C |
| Heat Deflection Temperature | 1.8MPa,Annealed | ASTMD648 | 95.0 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched Izod Impact Strength | 23°C,6.35mm | ISO180 | 200 | J/m |
| Notched Izod Impact Strength | 23°C,6.35mm | ASTMD256 | 200 | J/m |
| Hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R计秤,23°C | ASTMD785 | 110 | |
| Rockwell Hardness | R计秤,23°C | ISO2039-2 | 110 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating | 1.5mm,AllColors | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.