Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Density / Specific Gravity | | ISO1183 | 1.41 | g/cm³ |
| Melt Mass-Flow Rate | | ASTMD1238 | 9.0 | g/10min |
| Melt Mass-Flow Rate | | ISO1133 | 9.0 | g/10min |
| Melt Volume flow Rate | 190°C/2.16kg | ISO1133 | 8.00 | cm3/10min |
| Modeling Shrinkage | TD:2.00mm | ISO294-4 | 2.0 | % |
| Modeling Shrinkage | MD:2.00mm | ISO294-4 | 2.0 | % |
| Moisture Absorption | 23°C,24hr | ISO62 | 0.50 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Modulus | | ISO527-2 | 2700 | Mpa |
| Tensile Stress | | ISO527-2 | 62.0 | Mpa |
| Nominal Tensile Strain at Break | | ISO527-2 | 35 | % |
| Flexural Modulus | | ISO178 | 2500 | Mpa |
| Flexural Stress | | ISO178 | 87.0 | Mpa |
| Coefficient of Friction | Dynamic2 | JISK7218 | 0.37 | |
| Coefficient of Friction | Steel - Dynamic3 | JISK7218 | 0.46 | |
| Coefficient of Friction | Steel - Dynamic4 | JISK7218 | 0.40 | |
| Specific Wear Rate | 0.98MPa,0.30m/sec5 | JISK7218 | <1.0 | 10^-8mm³/N·m |
| Specific Wear Rate | 0.49MPa,0.30m/sec5 | JISK7218 | <1.0 | 10^-8mm³/N·m |
| Specific Wear Rate | 0.98MPa,0.30m/sec6 | JISK7218 | 30 | 10^-8mm³/N·m |
| Specific Wear Rate | 0.49MPa,0.30m/sec6 | JISK7218 | 65 | 10^-8mm³/N·m |
| Specific Wear Rate | 0.060MPa,0.15m/sec7 | JISK7218 | 3500 | 10^-8mm³/N·m |
| Specific Wear Rate | 0.060MPa,0.15m/sec8 | JISK7218 | 6500 | 10^-8mm³/N·m |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Heat Deflection Temperature | 1.8MPa,Unannealed | ISO75-2/A | 95.0 | °C |
| Coefficient of Linear Thermal Expansion | MD：23to55°C | 内部方法 | 1.2E-04 | cm/cm/°C |
| Coefficient of Linear Thermal Expansion | TD：23to55°C | 内部方法 | 1.2E-04 | cm/cm/°C |
| Electrical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface Resistivity | | IEC60093 | 1E+16 | ohms |
| Volume Resistivity | | IEC60093 | 1E+14 | ohms·cm |
| Dielectric Strength | 3.00mm | IEC60243-1 | 19 | KV/mm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 6.0 | kJ/m² |
| Hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | M-Scale | ISO2039-2 | 80 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Flame Rating | | UL94 | HB | |
| Additional | Test Condition | Test Method | Test Result | Unit |
|---|
| Color Number | | | CF2001/CD3068 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.