Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Mass-Flow Rate | 200℃, 5kg | ISO 1133-1 | 2 | g/10min |
| Melt Mass-Flow Rate | 220℃, 10kg | ISO 1133-1 | 20 | g/10min |
| Modeling Shrinkage | 23℃ | ISO 2577 | 0.4-0.7 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile Strength | 50mm/min | ISO 527-2 | 47 | Mpa |
| Break | 50mm/min | ISO 527-2 | 8 | % |
| Flexural Strength | 2mm/min | ISO 178 | 76 | Mpa |
| Flexural Modulus | 2mm/min | ISO 178 | 2500 | Mpa |
| Rockwell Hardness | | ISO 2039-2 | 108 | R scale |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load | 0.45MPa | ISO 75-2 | 85 | °C |
| Deflection Temperature Under Load | 1.8MPa | ISO 75-2 | 77 | °C |
| Vicat Softening Temperature | 1kg, 120℃/h | ISO 306 | 96 | °C |
| Vicat Softening Temperature | 5kg, 50℃/h | ISO 306 | 86 | °C |
| Electrical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume Resistivity | | IEC 60093 | 100000000000000 | ohms·cm |
| Dielectric Strength | | IEC 60243-1 | 22 | KV/mm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Notched Izod Impact Strength | | | | |
| Notched Izod Impact Strength | 23℃ | ISO 180 | 20 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.