Technical Data Sheet
Physical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Melt Mass-Flow Rate | 300°C/1.2kg | ASTMD1238 | 10 | g/10min |
Modeling Shrinkage | MD:3.20mm | 内部方法 | 0.60to0.80 | % |
Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Tensile Modulus | | ASTMD638 | 2280 | Mpa |
Tensile Strength | Yield | ASTMD638 | 62.1 | Mpa |
Tensile Strength | Break | ASTMD638 | 65.5 | Mpa |
Tensile Elongation | Yield | ASTMD638 | 6.0 | % |
Tensile Elongation | Break | ASTMD638 | 130 | % |
Flexural Modulus | 50.0mmSpan | ASTMD790 | 2340 | Mpa |
Flexural Strength | Yield,50.0mmSpan | ASTMD790 | 101 | Mpa |
Thermal Properties | Test Condition | Test Method | Test Result | Unit |
---|
Heat Deflection Temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 138 | °C |
Heat Deflection Temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 127 | °C |
Vicat Softening Temperature | | ASTMD15255 | 143 | °C |
Coefficient of Linear Thermal Expansion | MD:-40to40°C | ASTME831 | 6.7E-05 | cm/cm/°C |
Coefficient of Linear Thermal Expansion | TD:-40to40°C | ASTME831 | 6.7E-05 | cm/cm/°C |
RTIElec | | UL746 | 130 | °C |
RTIImp | | UL746 | 120 | °C |
RTIStr | | UL746 | 130 | °C |
Electrical Properties | Test Condition | Test Method | Test Result | Unit |
---|
Arc Resistance | | ASTMD495 | PLC7 | |
Comparative Tracking Index | CTI | UL746 | PLC2 | |
High Amp Arc Ignition | HAI | UL746 | PLC3 | |
High Voltage Arc Tracking Rate | HVTR | UL746 | PLC4 | |
Hot-wire Ignition | HWI | UL746 | PLC2 | |
Impact Properties | Test Condition | Test Method | Test Result | Unit |
---|
Instrumented Dart Impact | 23°C,TotalEnergy | ASTMD3763 | 73.4 | J |
Flammability | Test Condition | Test Method | Test Result | Unit |
---|
Flame Rating | 0.8mm | UL94 | V-2 | |
Flame Rating | 1.1mm | UL94 | V-0 | |
Flame Rating | 3.0mm | UL94 | 5VA | |
Glow Wire Flammability Index | 1.0mm | IEC60695-2-12 | 960 | °C |
Glow Wire Ignition Temperature | 1.0mm | IEC60695-2-13 | 875 | °C |
Oxygen Index | | ISO4589-2 | 35 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.